Low Cost Piezoelectric Disc Transducer for Non-destructive Testing
Product Description
Low Cost Piezoelectric Disc Transducer for Non-destructive Testing
WuHan Piezohannas Tech.Co .,Ltd is a manufactuer of piezoelectric ceramics ,ultrasonic transducers with strong technology force.With a quality management system and research & development sector,our products are extensively used in most applications.
PZT4 material piezo disks |
piezoelectric disk transducer |
piezo disc for Non-destructive Testing |
Size:
Thickness:4mm
Material:P-41
Standard Size of Piezo Discs:
range of piezo disc to produce:
Diameter: 2mm-120mm
Thickness:0.1mm-30mm
Applications:
Piezoelectric materials have excellent force-electric coupling properties and are widely used in the field of non-destructive testing. The piezoelectric vibration nondestructive testing technology has the following characteristics: 1) it id sensitive to small internal damage of large structures; 2) stable and reliable, wide linear range of operation, able to adapt to more complicated working conditions; 3) more reliable stability .The subsequent data processing is simple. This paper presents the overall design of the piezoelectric non-destructive testing device.
The field of Nondestructive Testing (NDT) is a very broad, interdisciplinary field that plays a critical role in assuring that structural components and systems perform their function in a reliable and cost effective fashion. NDT technicians and engineers define and implement tests that locate and characterize material conditions and flaws that might otherwise cause planes to crash, reactors to fail, trains to derail, pipelines to burst, and a variety of less visible, but equally troubling events. These tests are performed in a manner that does not affect the future usefulness of the object or material. In other words, NDT allows parts and material to be inspected and measured without damaging them. Because it allows inspection without interfering with a product's final use, NDT provides an excellent balance between quality control and cost-effectiveness. Generally speaking, NDT applies to industrial inspections. The technologies that are used in NDT are similar to those used in the medical industry, but nonliving objects are the subjects of the inspections.
Typical value of "Hard" PZT materials performance：
Hard" PZT materials |
PZT-41 |
PZT-42 |
PZT-43/4D |
PZT-82 |
PBaS-4 |
||
Dielectric Constant |
ɛTr3 |
1050 |
1250 |
1420 |
1100 |
1900 |
|
Coupling factor |
KP |
0.58 |
0.58 |
0.58 |
0.52 |
0.59 |
|
K31 |
0.32 |
0.33 |
0.34 |
0.3 |
0.34 |
||
K33 |
0.66 |
0.67 |
0.68 |
0.57 |
0.68 |
||
Kt |
0.48 |
0.48 |
0.48 |
0.4 |
0.49 |
||
Piezoelectric coefficient |
d31 |
10-12m/v |
-106 |
-124 |
-138 |
-100 |
-160 |
d33 |
10-12m/v |
260 |
280 |
300 |
240 |
380 |
|
g31 |
10-3vm/n |
-11.4 |
-11.2 |
-11 |
-10.3 |
-9.5 |
|
g33 |
10-3vm/n |
28 |
25.3 |
24 |
25 |
22.6 |
|
Frequency coefficients |
Np |
2280 |
2200 |
2160 |
2280 |
2200 |
|
N1 |
1671 |
1613 |
1583 |
1671 |
1613 |
||
N3 |
1950 |
1900 |
1875 |
1950 |
1850 |
||
Nt |
2250 |
2200 |
2200 |
2300 |
2200 |
||
Elastic compliance coefficient |
Se11 |
10-12m2/n |
11.8 |
12.7 |
13.2 |
11.6 |
13.2 |
Machanical quality factor |
Qm |
1000 |
800 |
600 |
1200 |
2200 |
|
Dielectric loss factor |
Tg δ |
% |
0.3 |
0.4 |
0.5 |
0.3 |
0.5 |
Density |
ρ |
g/cm3 |
7.5 |
7.5 |
7.5 |
7.6 |
7.5 |
Curie Temperature |
Tc |
°C |
320 |
320 |
320 |
310 |
310 |
Young's modulus |
YE11 |
<109N/m3 |
85 |
79 |
76 |
86 |
76 |
Poison Ratio |
0.3 |
0.3 |
0.3 |
0.3 |
0.33 |